RESITAN RGP 2000G OrthoPhthalic
This resin is characterized by its easy application, low color, low viscosity, moderate gel time, good adhesion to glass fiber and relatively high reactivity .Composite parts made of this resin and glass fiber reinforcement have very good physical and mechanical properties application. Resitan RGP 2000G Is used for manufacturing of composite parts, such as reservoirs, structural panels, boat and automotive parts.
Non-volatile = 63±2 % Viscosity = 450-550 mpa.s
Gel time( 25°C-35°C) = 15-30 min Peak Temperature = 130-140°C
Description
RESITAN RGP2000G is a general-purpose unsaturated ortho - polyester resin.
Applications
RESITAN RGP 2000G is suggested for manufacturing of
composite parts such as reservoirs, structural panels,
boats and automobile parts.
Specifications
Non-volatile 63 ±2 %
Appearance Clear
Acid Value 19 – 25 mgKOH/g
Color max.1 Gardner
Viscosity @ 25 C:
rotary 450-550 mpa.s
DIN CUP4 85 – 105 Sec
Curing condition with 0.5% Co (1%) and 2% MEKP (50%):
Gel time (25 -35C) 15 – 30 min
Curing time (35 – Tpeak) 6 – 13 min
Peak Temperature 120-150 ºC
Shelf Life
6 months @ Storage Condition.
Storage Conditions
This resin must be kept in a cool place, properly 5-20 ºC, in closed drums. Keep away from any source of heat and direct sunlight. Temperature higher than 25 ºC or direct sunlight decreases shelf life of Resin.
Also this resin is flammable and must be keep away from any ignition sources or flame.
Safety Precautions
Avoid direct contact with skin and eyes.
Necessary eye and body protection should be used.
Apply good ventilation in working area
Never mix cobalt solution and MEKP together directly because explosion maybe occurs.
Packaging
steel drums of 200Kg net
Type Of Monomer
Styrene
Note
The information given above is correct to the best of our knowledge without any guarantee. Users should determine the suitability of this product for their purposes by arranging appropriate tests. Resitan company do not accept any liability for loss or damage caused by this product.
|